PM200 is a diisocyanate-diphenylmethane(MDI)-based composition containing some higher functionality isocyanates. The functionality is about 2.6-2.7. It is abrown liquid at ambient temperatures.
MR200 can be widely used in the production of rigid PU foam heat-insulating materials; also used in isocyanurate foam, paints, adhesives, structural foam,cellular integral skin foam, automotive bumper and interior parts, high-resilience foam and synthetic wood, etc. Due to its unique composition structure, MR200 can provide better flowability. It is, therefore, particularly suitable for the production which require strict flowability of systems.
Certificate of Analysis
| Testing Items |
Specifications |
Results |
| Appearance |
Brown Liquid |
Conformity |
| Viscosity(25ºC)/(mPa·S) |
150-250 |
202 |
| NCO Content/% |
30.5-32.0 |
31.21 |
| Hydrolysable Chlorides/% |
<=0.20 |
0.06 |
| Acid Content |
<=0.030 |
0.004 |
| Density(25ºC)/(g/cm^3) |
1.220-1.250 |
1.233 |
| Qualitied |
Storage
Since PM200 is a reactive chemical, reaction with atmospheric moisture happens easily and leads to the formation of insoluble ureas and carbon dioxide gas, which can result in pressure build-up in closed containers and viscosity increase of the product.Containers must therefore be absolutely dry and carefully sealed after congested with nitrogen.
Containers of MR200 should be kept properly closed and stored indoors at ambient temperature (15-35ºC) in a well-ventilated area. Storage at low temperature (below5ºC) may lead to some crystallization; this material must, therefore, be protected from frost.If crystallization does occur, the material should be heated by rolling the drum in a hot air oven at 70-80ºC to melt it out, and should then be thoroughly agitated before use. Melting in a water bath is not recommended.
Extended storage at temperatures above 50ºC is not recommended to prevent from the formation of insoluble solids and viscosity increase.